GB/T 35804-2018 硫化橡胶或热塑性橡胶 耐臭氧龟裂 测定试验箱中臭氧浓度的试验方法
简介：
信息：ICS：83.060 CCS：G40 发布：2018-02-06 00:00:00.0 实施：2018-09-01 00:00:00.0

ISO 1431-1-2004 硫化或热塑性橡胶.耐臭氧龟裂.第1部分:静态和动态应变试验
简介：This part of ISO 1431 specifies procedures intended for use in estimating the resistance of vulcanized or thermoplastic rubbers to cracking when exposed, under static or dynamic tensile strain, to air containing a definite concentration of ozone and at a definite temperature in circumstances that exclude the effects of direct light.Great caution is necessary in attempting to relate standard test results to service performance since the relative ozone resistance of different rubbers can vary markedly depending on the conditions, especially ozone concentration and temperature. In addition, tests are carried out on thin test pieces deformed in tension and the significance of attack for articles in service can be quite different owing to the effects of size and of the type and magnitude of the deformation. Explanatory notes on the nature of ozone cracking are given in Annex A.Reference and alternative methods for determining the ozone concentration are described in ISO 1431-3.
信息：ICS：83.060 CCS：G34 发布：2004-09 实施：

GB/T 13642-2015 硫化橡胶或热塑性橡胶 耐臭氧龟裂 动态拉伸试验
简介：本标准规定了硫化橡胶或热塑性橡胶在动态拉伸应变下,暴露于含一定浓度臭氧的空气中和在规定温度且无光线直接影响下的环境中进行的耐臭氧龟裂的试验方法。本标准适用于硫化橡胶或热塑性橡胶。
信息：ICS：83.060 CCS：G40 发布：2015-05-15 实施：2015-10-01

SANS 11431-3-2003 硫化或热塑性橡胶，耐臭氧龟裂．第3部分：实验室试验箱内测定臭氧浓度的推荐的和可选用的方法
简介：Describes three types of method for the determination of ozone concentration in laboratory test chambers, i.e. a method for UV absorption, a method for instrumental techniques and a method for wet-chemical techniques.
信息：ICS：83.060 CCS：G34 发布：2003-05-30 实施：

GB/T 7762-2014 硫化橡胶或热塑性橡胶 耐臭氧龟裂 静态拉伸试验
简介：本标准规定了硫化橡胶或热塑性橡胶在静态拉伸应变下,暴露于含一定浓度臭氧的空气中和在规定温度且无光线直接影响下的环境中进行的耐臭氧龟裂的试验方法。本标准适用于硫化橡胶或热塑性橡胶。
信息：ICS：83.060 CCS：G40 发布：2014-12-22 实施：2015-06-01

BS ISO 1431-3-2000 硫化橡胶或热塑橡胶.耐臭氧龟裂性.在实验室试验测定臭氧浓度的标准方法和替用方法
简介：This part of ISO 1431 describes three types of method for the determination of ozone concentration in laboratory test chambers.Method A —UV absorption: this is the reference method, and is used as the means of calibration for the alternative methods B and C.Method B —Instrumental techniques:B1: electrochemicalB2: chemiluminescenceMethod C —Wet-chemical techniques:Procedure Ⅰ Procedure Ⅱ Procedure Ⅲ
信息：ICS：83.060 CCS：G34 发布：2000-06-15 实施：2000-06-15

GB/T 7762-2003 硫化橡胶或热塑性橡胶 耐臭氧龟裂静态拉伸试验
简介： 本标准规定了硫化橡胶或热塑性橡胶在静态拉伸应变条件下，暴露于含一定浓度臭氧的空气中和在规定温度且无光线直接影响的环境中进行的耐臭氧龟裂的试验方法。 不同橡胶材料的耐臭氧能力随臭氧浓度和温度的不同有明显差别。拉伸应变的试样进行臭氧试验和使用中的制品受臭氧的作用而产生的破坏程度，由于尺寸、类型和应变大小的不同有很大差别。 关于臭氧龟裂性质的注释参见附录A。
信息：ICS：83.060 CCS：G40 发布：2003-01-10 实施：2003-07-01

ISO 1431-3-2000 硫化或热塑性橡胶 耐臭氧龟裂 第3部分:实验室试验箱内测定臭氧浓度的推荐的和可选用的方法
简介：This part of ISO 1431 describes three types of method for the determination of ozone concentration in laboratory test chambers.Method A — UV absorption: this is the reference method, and is used as the means of calibration for the alternative methods B and C.Method B — Instrumental techniques:B1: electrochemical B2: chemiluminescence Method C — Wet-chemical techniques:Procedure Ⅰ Procedure Ⅱ Procedure Ⅲ
信息：ICS：83.060 CCS：G34 发布：2000-04 实施：

BS ISO 1431-3-2017 硫化橡胶或热塑橡胶.耐臭氧龟裂性.在实验室试验测定臭氧浓度的标准方法和替用方法
简介：
信息：ICS：83.060 CCS：G34 发布：2017-07-20 实施：2017-07-31

JIS K6404-19-1999 橡胶或塑料涂覆织物的试验方法.第19部分:耐臭氧龟裂的测定
简介：この規格は，ゴム又はプラスチック引布の静的条件におけるオゾン劣化試験方法について規定する。試験は直射日光の当たらないところで,静的圧力の下で，オゾンを含む空気にさらされたとき，ゴム又はプラスチック引布のき裂の発生に対する相対的な耐性を測定することを意図したものである。すべての老化試験と同様に，オゾン劣化試験は，同じ組成，同じ用途の品物の比較の手段として考えるべきであるが，絶対的な基準としてみなすべきではない。この試験は，ある基布がある種の劣化と比較して与えられる限界を上回る耐性を獲得している場合の検査の手段に過ぎないものとみなすことによって，この試験の意義を限定することが望ましい。 これらの点を考慮に入れるならば，試験に際して得られた結果を製品の耐用期間を予測するものとして見ることはできない。
信息：ICS：59.080.40 CCS：W59 发布：1999-07-20 实施：

DIN ISO 1431-1-2017 硫化或热塑性橡胶.耐臭氧龟裂.第1部分:静态和动态应变试验(ISO 1431-1-2012)
简介：
信息：ICS：83.060 CCS：G35 发布：2017-04 实施：

HG/T 2716-1995 橡胶或塑料涂覆织物.静态耐臭氧龟裂性能的测定
简介：本标准规定了橡胶或塑料涂覆织物静态而臭氧龟裂性能的测定方法。 本标准适用于橡胶或塑料涂覆织物在静态应变状态下暴露于含有规定浓度、温度、湿度的臭氧空气中，并在无直射阳光存在的环境下进行老化试验。
信息：ICS： CCS：W59 发布：1995-05-09 实施：1996-01-01

BS ISO 1431-1-2012 硫化橡胶或热塑性橡胶.耐臭氧龟裂性.静态和动态应变试验
简介：
信息：ICS：83.060 CCS：G34 发布：2012-11-30 实施：2012-11-30

ISO 1431-2-1994 硫化或热塑性橡胶 耐臭氧龟裂 第2部分:动态应变试验
简介：
信息：ICS：83.060 CCS：G34 发布：1994-01 实施：

BS ISO 1431-1-2012 硫化橡胶或热塑性橡胶.耐臭氧龟裂性.静态和动态应变试验
简介：
信息：ICS：83.060 CCS：G34 发布：2012-11-30 实施：2012-11-30

ISO 1431-1-1989 硫化或热塑性橡胶 耐臭氧龟裂 第1部分:静态应变试验
简介：
信息：ICS：83.060 CCS：G34 发布：1989-06 实施：1989-06-15

NF T46-019-1-2012 硫化或热塑性橡胶.耐臭氧龟裂.第1部分:静态和动态应变测试
简介：
信息：ICS：83.060 CCS：G34 发布：2012-11-01 实施：2012-11-17

DS/ISO 1431-1-1989 硫化或热塑性橡胶.耐臭氧龟裂性.第1部分:静态应变试验
简介：This International Standard is intended for use in estimating the resistance of vulcanized rubbers to cracking when exposed, under static tensile strain, to air containing a definite concen tration of ozone and at a definite temperature in circumstances where the effects of direct light are excluded.Great caution is necessary in attempting to relate standard test results to service performance since the relative ozone resistance of different vulcanizates can vary markedly according to conditions, especially ozone concentration and temperature. In addition, tests are carried out on thin test pieces deformed in tension and the significance of attack for articles in service may be quite different owing to the effects of size and the type and magnitude of deformation. Explanatory notes on the nature of ozone cracking are given in the annex.Methods for determining resistance to ozone cracking under dynamic strain conditions and combined dynamic and static strain conditions will form the subject of Part 2 of this International Standard. A reference method for estimating the ozone concentration will form the subject of Part 3 of this inter national Standard.
信息：ICS：825 CCS： 发布：1989 实施：

DIN ISO 1431-3-2011 硫化或热塑性橡胶.耐臭氧龟裂.第3部分:实验室试验箱内测定臭氧浓度的参考和可选用的方法(ISO 1431-3-2000)
简介：This part of ISO 1431 describes three types of method for the determination of ozone concentration in laboratory test chambers. Method A - UV absorption: this is the reference method, and is used as the means of calibration for the alternative methods B and C. Method B - Instrumental techniques: B1: electrochemical, B2: chemiluminescence. Method C - Wet-chemical techniques: Procedure I, Procedure II, Procedure III
信息：ICS：83.060 CCS：G35 发布：2011-05 实施：

JUS G.S2.138-1985 硫化橡胶．耐臭氧龟裂性．静应变检测
简介：
信息：ICS： CCS： 发布：1985-01-01 实施：

DIN ISO 1431-1-2011 硫化或热塑性橡胶.耐臭氧龟裂.第1部分:静态和动态应变试验(ISO 1431-1-2004 + 修改件1-2009)
简介：This part of ISO 1431 specifies a procedure intended for use in estimating the resistance of vulcanized or thermoplastic rubbers to cracking when exposed, under static or dynamic tensile strain, to air containing a definite concentration of ozone and at a definite temperature in circumstances that exclude the effects of direct light. Great caution is necessary in attempting to relate standard test results to service performance since the relative ozone resistance of different rubbers can vary markedly depending on the conditions, especially ozone concentration and temperature. In addition, tests are carried out on thin test pieces deformed in tension and the significance of attack for articles in service can be quite different owing to the effects of size and of the type and magnitude of the deformation. Explanatory notes on the nature of ozone cracking are given in Annex A.
信息：ICS：83.060 CCS：G35 发布：2011-05 实施：

ISO 1431-2-1982 硫化橡胶.耐臭氧龟裂性.第2部分:动态应变试验
简介：
信息：ICS：6839 CCS：G34 发布：1982-08 实施：

KS M ISO 1431-1-2009 硫化橡胶或热塑橡胶.耐臭氧龟裂性.第1部分:静态应变试验
简介：이 표준은 직접적인 빛의 영향을 받지 않는 환경에서의 설정된 온도와 오존 농도를 포함하는
信息：ICS：83.06 CCS：G34 发布：2009-12-11 实施：2009-12-11

KS M ISO 1431-1-2009 硫化橡胶或热塑橡胶.耐臭氧龟裂性.第1部分:静态应变试验
简介：이 표준은 직접적인 빛의 영향을 받지 않는 환경에서의 설정된 온도와 오존 농도를 포함하는
信息：ICS：83.06 CCS：G34 发布：2009-12-11 实施：2009-12-11

KS M ISO 1431-3-2009 硫化橡胶或热塑橡胶.耐臭氧龟裂性.第3部分:实验室测定臭氧浓度的基准和交替方法
简介：이 표준은 실험실 시험 챔버에서 오존 농도를 측정하기 위한 3가지 종류의 방법을 명시한다.
信息：ICS：83.060 CCS：G34 发布：2009-07-28 实施：2009-07-28

KS M ISO 1431-3-2009 硫化橡胶或热塑橡胶.耐臭氧龟裂性.第3部分:实验室测定臭氧浓度的基准和交替方法
简介：이 표준은 실험실 시험 챔버에서 오존 농도를 측정하기 위한 3가지 종류의 방법을 명시한다.
信息：ICS：83.060 CCS：G34 发布：2009-07-28 实施：2009-07-28

ISO 1431-1 AMD 1-2009 硫化或热塑性橡胶.耐臭氧龟裂.第1部分:静态和动态应变试验.修改件1
简介：
信息：ICS：83.060 CCS：G34 发布：2009-03 实施：

HG/T 2716-2008 橡胶或塑料涂覆织物.静态耐臭氧龟裂性能的测定
简介：警告：使用本标准的人员应熟悉正规实验室操作规程。本标准无意涉及因使用本标准而可能出现的所有安全问题。制定安全和健康制度并确保符合国家法规是使用者的责任。本标准规定了橡胶或塑料涂覆织物在静态条件下耐臭氧龟裂的测定方法。本标准适用于橡胶或塑料涂覆织物在静态应变状态下暴露于无直射阳光、含臭氧的空气中时的相对耐臭氧龟裂性能的测定。与所有的老化试验一样，耐臭氧试验应被认为是相同组分和用途的制品对比的一种手段,但不是绝对的判断标准。最好是限定试验的意义，即仅将试验理解为与某种降解相比较织物获得优于给定临界值的耐臭氧龟裂性能时的一种控制手段。基于这种观点，试验所得的结果尚不能用于预测制品的寿命长短。
信息：ICS：59.080.40 CCS：G30;G42 发布：2008-04-23 实施：2008-10-01

CNS 10018-2008 硫化橡胶或热塑性橡胶耐臭氧龟裂性试验法(静态及动态应变试验)
简介：
信息：ICS：80.060 CCS： 发布：2008-01-14 实施：

NF T46-019-3-2006 硫化或热塑性橡胶.耐臭氧龟裂.第3部分:实验室试验箱内测定臭氧浓度的参考和交替方法
简介：
信息：ICS：83.060 CCS：G40 发布：2006-11-01 实施：2006-11-05

KS M 6790-2005 硫化橡胶耐臭氧龟裂性试验方法
简介：이 규격은 가황 고무의 오존 노화를 측정하는 시험 방법에 대하여 규정한다.
信息：ICS：83.06 CCS：G31 发布：2005-05-27 实施：2005-05-27